炼钢RH 精炼炉用耐火材料无铬化的实现

炼钢RH精炼炉用耐火材料无铬化的实现 ·1·

炼钢RH精炼炉用耐火材料无铬化的实现

赵 明沈钟铭

(宝钢股份炼钢厂,上海 201900)

摘 要 宝钢股份炼钢厂自2008年研制出无铬的整体浇注浸渍管后,不断推进RH槽体内壁无铬化耐火材料的开发和应用,逐步实现了不烧无铬砖、整体浇注管对RH浸渍管、环流管、下部槽和中上部槽镁铬质耐火材料的替代。工业应用试验结果表明,RH精炼炉寿命业绩获得进步,降低了成本消耗。至2012年底,宝钢炼钢厂全面实现了RH精炼炉用无铬耐火材料的工业化应用。 关键词 RH耐火材料 镁铬砖 无铬化

Chromium-free Refractory Achievement on RH Degasser

Zhao Ming Shen Zhongming

(Steel-making Plant, Baosteel Co., Ltd., Shanghai, 201900)

Abstract In 2008, Steel-making Plant of Baosteel Co.,Ltd., succeeded in developing the chromium-free monolithic casting RH immersion snorkels. After that, Baosteel has been promoting the development and application of chromium-free refractory on RH degasser's vessel lining and has gradually carried out the replacement of magnesia-chrome refractory on RH immersion & circulating snorkels, lower vessels, middle & upper vessels with chromium-free magnesia brick, monolithic casting snorkels. The service life has been greatly improved and the refractory cost and consumption of RH vessel have decreased through industrial application. By the end of 2012, Steel-making Plant of Baosteel Co.,Ltd., has achieved success in the fully industrial application of chromium-free refractory on all RH degasser vessels. Key words RH refractories, Magnesia-chrome brick, Chromium-free refractories

1 前言

RH真空精炼技术是一种操作简单、经济有效的二次精炼技术,其功能已发展到脱气净化、吹氧脱碳、造渣脱硫脱磷和合金化,相应地,对RH精炼炉用耐火材料要求也越来越高。RH精炼炉用耐火材料,从早期的高铝质耐火材料发展到普通烧成镁铬质耐火材料,后进一步采用直接结合镁铬砖、半再结合或再结合镁铬砖。为应对严苛的使用环境,在下部槽、环流管等RH关键部位应用的高纯再结合镁铬砖中氧化铬含量高达24% [1]。

近年来,欧美、日韩和台湾的钢铁企业为顺应环保需求,减少镁铬砖制造过程和RH 冶炼过程所形成的致癌物质六价铬,均在积极推进RH精炼炉用耐火材料无铬化,实现了局部生产应用[2]。宝钢是国内较早开展这项工作的钢铁企业,经过几年的努力,完成了RH耐火材料全面无铬化。

本文重点介绍宝钢股份炼钢厂RH精炼炉用耐火材料无铬化实现过程。

赵明, 男, 硕士, 高级工程师, 从事耐火材料应用

炼钢RH 精炼炉用耐火材料无铬化的实现

炼钢RH 精炼炉用耐火材料无铬化的实现

, mingzhao@http://www.51wendang.com

相关文档
热门文档
你可能喜欢
  • 炉用耐火材料
  • 耐火材料
  • 耐火材料应用
  • 耐火钢
  • 耐火极限
  • 耐火试验
  • RH真空
评论